D-orbital ordering of oxygen-deficient amorphous and anatase TiO 2-x channels for high mobility thin film transistors

Kwang Hyuk Choi, Kwun Bum Chung, Han Ki Kim

Research output: Contribution to journalArticlepeer-review

25 Scopus citations

Abstract

Semiconducting behavior in oxygen-deficient amorphous and anatase TiO 2-x films prepared by direct current magnetron sputtering was investigated for high mobility oxide thin film transistors (OxTFTs). Rapid thermal annealing (RTA) was found to induce transition from an amorphous to anatase phase in oxygen-deficient TiO2-x channels and was significantly influenced by DC power during sputtering. Compared to the low field effect mobility (μFE: 0.57 cm2/V s) of OxTFTs with d-orbital ordered amorphous TiO2-x channels, OxTFTs with anatase TiO2-x channels exhibited a higher mobility (μFE: 1.02 cm2/V s) due to an increased amount of free carriers and effective d-orbital ordering. In addition, the oxygen ambient annealing time during the RTA process had a critical effect on Von shift and shallow/deep trap states of anatase TiO2-x-based TFTs.

Original languageEnglish
Article number153511
JournalApplied Physics Letters
Volume102
Issue number15
DOIs
StatePublished - 15 Apr 2013

Fingerprint

Dive into the research topics of 'D-orbital ordering of oxygen-deficient amorphous and anatase TiO 2-x channels for high mobility thin film transistors'. Together they form a unique fingerprint.

Cite this