Effect of co-sensitization in solar exfoliated TiO 2 functionalized rGO photoanode for dye-sensitized solar cell applications

K. Ashok Kumar, K. Subalakshmi, J. Senthilselvan

Research output: Contribution to journalArticlepeer-review

46 Scopus citations

Abstract

In this report graphene oxide is successfully prepared by modified Hummers’ method at room temperature without using low temperature ice bath reactor. For the fabrication of DSSC photoanode, rGO-TiO 2 nanocomposite was prepared using a novel two step hydrothermal and solar exfoliation process. Formation of anatase TiO 2 with tetragonal structure is confirmed using XRD pattern. Peak splitting occurs in Raman 2D band indicates the presence of bi-layer rGO. FESEM and HRTEM studies show the synthesized spherical shaped TiO 2 nanoparticles embedded on rGO flakes and the average particulate size is found to be c.a 10 nm. FTIR and XPS results confirm the formation of direct bonding between Ti and C atoms in rGO-TiO 2 by the observation of vibrational band at 1124 cm −1 and binding energy at 284.13 eV respectively. DSSC devices are fabricated and EIS measurements are performed to determine interfacial charge transfer kinetics such as chemical capacitance, recombination resistance and electron lifetime. Here, we report for the first time the results on the co-sensitization of solar exfoliated rGO-TiO 2 as photoanode using a combination of metal-free and metal-based organic dyes. Enhanced PCE of 6.9% is realized in N719 + N3 co-sensitized DSSC by its increased electron recombination lifetime.

Original languageEnglish
Pages (from-to)104-115
Number of pages12
JournalMaterials Science in Semiconductor Processing
Volume96
DOIs
StatePublished - 15 Jun 2019

Keywords

  • Bi-layer rGO
  • Co-sensitization
  • DSSC and Electrochemical impedance spectroscopy
  • rGO‐TiO

Fingerprint

Dive into the research topics of 'Effect of co-sensitization in solar exfoliated TiO 2 functionalized rGO photoanode for dye-sensitized solar cell applications'. Together they form a unique fingerprint.

Cite this