Abstract
Olivine-type LiFePO4/C cathode materials are fabricated with FePO4 powders that are pre-synthesized by two different processes from iron chloride solution. Process I is a modified precipitation method which is implemented by the pH control of a solution using NH4OH to form FePO4 precipitates at room temperature. Process II is a conventional precipitation method, of which H3PO4 (85%) solution is gradually added to a FeCl3 solution during the process to maintain a designated mole ratio. The solution is subsequently aged at 90°C in a water bath until FePO4 precipitates appear. In order to synthesize LiFePO4/C composites, each batch of FePO4 powders is then mixed with pre-milled lithium carbonate and glucose (8 wt. %) as a carbon source in a ball-mill. The structural characteristics of both LiFePO4/C composites fabricated using iron phospates from two different routes have been examined employing XRD and SEM. The modified precipitation process is considered to be a relatively simple and effective process for the preparation of LiFePO4/C composites owing to their excellent electrochemical properties and rate capabilities.
Original language | English |
---|---|
Pages (from-to) | 187-193 |
Number of pages | 7 |
Journal | Electronic Materials Letters |
Volume | 9 |
Issue number | 2 |
DOIs | |
State | Published - Mar 2013 |
Keywords
- amorphous material
- composite material
- industrial waste
- lithium iron phosphate
- precipitation