Abstract
The influence of co-existing gases on the hydrogen permeation was studied through a Pd-coated V89.8Cr10Y0.2 alloy membrane. Preliminary hydrogen permeation experiments have been confirmed that hydrogen flux was 6.26 ml/min/cm2 for a Pd-coated V 89.8Cr10Y0.2 alloy membrane (thick: 0.5 mm) using pure hydrogen as feed gas. Also, the hydrogen permeation flux decreased with decrease of hydrogen partial pressure at constant pressure when H 2/CO2 and H2/CO2/H2S mixture applied as feed gas respectively and permeation fluxes were satisfied with Sievert's law in different feed conditions. It was found from XRD and SEM results after permeation test that the Pd-coated V89.8Cr 10Y0.2 alloy membrane had good stability and durability for various mixture feeding conditions.
Original language | English |
---|---|
Pages (from-to) | 6085-6091 |
Number of pages | 7 |
Journal | International Journal of Hydrogen Energy |
Volume | 38 |
Issue number | 14 |
DOIs | |
State | Published - 10 May 2013 |
Keywords
- HS
- Hydrogen separation
- Long-term test
- V-Cr-Y
- Vanadium
- WGS