Oxygen permeation performance of Ba _0.5Sr _0.5Co _0.8Fe _0.2O _3-δ membrane after surface modification

The effect of minor surface modification on the performance of Ba _{0. 5}Sr _{0. 5}Co _{0. 8}Fe _{0. 2}O _3-δ membrane was evaluated in the temperature region from 700 to 850 °C. Oxygen permeation experiments were conducted according to membrane thickness (1. 0mm and 1. 6 mm) and oxygen partial pressure (0. 21, 0. 42, and 0. 63 atm) in the absence and in the presence of carbon dioxide (300 and 500 ppm). The oxygen permeation flux of Ba _{0. 5}Sr _{0. 5}Co _{0. 8}Fe _{0. 2}O _3-δ membrane increased with increasing temperature and decreasing membrane thickness. The oxygen permeation flux through the membrane of 1. 0 mm thickness with Ba _{0. 5}Sr _{0. 5}Co _{0. 8}Fe _{0. 2}O _3-δ-modified surface was ca. 1. 23 ml/cm ²·min at 850 °C under air feeding condition. It was found that the Ba _{0. 5}Sr _{0. 5}Co _{0. 8}Fe _{0. 2}O _3-δ-modified Ba _{0. 5}Sr _{0. 5}Co _{0. 8}Fe _{0. 2}O _3-δ membrane has better oxygen permeation flux than the pristine Ba _{0. 5}Sr _{0. 5}Co _{0. 8}Fe _{0. 2}O _3-δ membrane. In summary, it has been demonstrated that the surface morphology is an important factor in determining the oxygen permeation fluxes through Ba _{0. 5}Sr _{0. 5}Co _{0. 8}Fe _{0. 2}O _3-δ membrane under mixed-control conditions.