Polyethylene Glycol-Assisted Engineering of NiCo₂S₄ Nanostructures for Enhanced Supercapacitor Performance

The development of high-performance electrode materials with controlled morphology remains a key challenge for advancing supercapacitor technologies. In this study, polyethylene glycol (PEG)-assisted hydrothermal synthesis was employed to engineer NiCo₂S₄ nanostructures with controlled morphology for enhanced supercapacitor performance. The influence of PEG concentration on nucleation behavior, structural evolution, and electrochemical characteristics was systematically investigated. The optimized NiCo₂S₄ electrode synthesized with 0.2% PEG (NiCoS-P2) exhibited a hierarchical flower-like nanosheet architecture with reduced agglomeration and improved electrochemically accessible surface area. As a result, the electrode delivered a high areal capacitance of 13.689 F/cm² (specific capacitance of 6845 F/g) at 5 mA/cm², along with excellent rate capability and superior cycling stability, retaining 84.16% capacitance after 12,000 cycles. Electrochemical analysis revealed that the charge storage process is predominantly diffusion-controlled with enhanced ion transport kinetics. Furthermore, an asymmetric supercapacitor device assembled using NiCoS-P2 as the positive electrode and activated carbon as the negative electrode demonstrated a wide operating voltage of 1.5 V, delivering an areal capacitance of 0.409 F/cm² (specific capacitance of 204.5 F/g), an energy density of 0.128 mWh/cm², and a power density of 2.99 mW/cm². The device also exhibited excellent long-term stability with 85.3% capacitance retention after 7000 cycles. This work highlights the effectiveness of polymer-assisted structural engineering in optimizing transition metal sulfide electrodes for advanced energy storage applications.: