Structures of delithiated and degraded LiFeBO3, and their distinct changes upon electrochemical cycling

Shou Hang Bo, Kyung Wan Nam, Olaf J. Borkiewicz, Yan Yan Hu, Xiao Qing Yang, Peter J. Chupas, Karena W. Chapman, Lijun Wu, Lihua Zhang, Feng Wang, Clare P. Grey, Peter G. Khalifah

Research output: Contribution to journalArticlepeer-review

27 Scopus citations

Abstract

Lithium iron borate (LiFeBO3) has a high theoretical specific capacity (220 mAh/g), which is competitive with leading cathode candidates for next-generation lithium-ion batteries. However, a major factor making it difficult to fully access this capacity is a competing oxidative process that leads to degradation of the LiFeBO3 structure. The pristine, delithiated, and degraded phases of LiFeBO3 share a common framework with a cell volume that varies by less than 2%, making it difficult to resolve the nature of the delithiation and degradation mechanisms by conventional X-ray powder diffraction studies. A comprehensive study of the structural evolution of LiFeBO3 during (de)lithiation and degradation was therefore carried out using a wide array of bulk and local structural characterization techniques, both in situ and ex situ, with complementary electrochemical studies. Delithiation of LiFeBO3 starts with the production of Li tFeBO3 (t ≈ 0.5) through a two-phase reaction, and the subsequent delithiation of this phase to form Lit-xFeBO3 (x < 0.5). However, the large overpotential needed to drive the initial two-phase delithiation reaction results in the simultaneous observation of further delithiated solid-solution products of Lit-xFeBO3 under normal conditions of electrochemical cycling. The degradation of LiFeBO3 also results in oxidation to produce a Li-deficient phase D-LidFeBO3 (d ≈ 0.5, based on the observed Fe valence of ∼2.5+). However, it is shown through synchrotron X-ray diffraction, neutron diffraction, and high-resolution transmission electron microscopy studies that the degradation process results in an irreversible disordering of Fe onto the Li site, resulting in the formation of a distinct degraded phase, which cannot be electrochemically converted back to LiFeBO3 at room temperature. The Li-containing degraded phase cannot be fully delithiated, but it can reversibly cycle Li (D-Lid+yFeBO3) at a thermodynamic potential of ∼1.8 V that is substantially reduced relative to the pristine phase (∼2.8 V).

Original languageEnglish
Pages (from-to)6585-6595
Number of pages11
JournalInorganic Chemistry
Volume53
Issue number13
DOIs
StatePublished - 7 Jul 2014

Fingerprint

Dive into the research topics of 'Structures of delithiated and degraded LiFeBO3, and their distinct changes upon electrochemical cycling'. Together they form a unique fingerprint.

Cite this